Aluminum base copper-clad laminate have excellent flame retardant, high mechanical strength, dimensional stability etc. Especially it has very good heat sink, electromagnetic shielding and solder float. It's widely used for the modifier and sparker on fire for motorcycle and mobile, power LED, sound box, power supply module and acoustics shielding system etc. Note: We specially produces Metal Base Copper-Clad Laminates, and our products have been compiled series with all complete specifications. The tapy and specification of Aluminum based Laminates CCAF-01, CCAF-04-A, CCAF-05etc. And 0.8mm, 1.0mm, 1.5mm, 2.0mm, etc. Thickness of the copper: 18um, 35um, 70um, 105um. Base size: 500mm ×, 600mm (20"×, 24"); 600mm ×, 1060mm (24"×, 42") CCAF-04-A Aluminum-base copper-clad laminate The test base: CCAF-04 the high heat dissipation Aluminum-base copper-clad laminate Thickness of the copper: 35um Thickness of the diclectric: 80um(matrial of the high heat dissipation) Thickness of the aluminum-base: 1.5mm The result of the test:
Aluminum base copper-clad laminate have excellent flame retardant, high mechanical strength, dimensional stability etc. Especially it has very good heat sink, electromagnetic shielding and solder float. It's widely used for the modifier and sparker on fire for motorcycle and mobile, power LED, sound box, power supply module and acoustics shielding system etc. Note: We specially produces Metal Base Copper-Clad Laminates, and our products have been compiled series with all complete specifications. The tapy and specification of Aluminum based Laminates CCAF-01, CCAF-04-A, CCAF-05etc. And 0.8mm, 1.0mm, 1.5mm, 2.0mm, etc. Thickness of the copper: 18um, 35um, 70um, 105um. Base size: 500mm ×, 600mm (20"×, 24"); 600mm ×, 1060mm (24"×, 42") CCAF-04-A Aluminum-base copper-clad laminate The test base: CCAF-04 the high heat dissipation Aluminum-base copper-clad laminate Thickness of the copper: 35um Thickness of the diclectric: 80um(matrial of the high heat dissipation) Thickness of the aluminum-base: 1.5mm The result of the test:
Item
Test item
Technology request
Unit
Test result
1
Peel Strength
A
≥ 1.0
N/mm
1.05
After thermal stress (260 ordm;C )
≥ 1.0
N/mm
1.05
2
Blister test AfterThermal stress (288 ordm;C, 2min)